1.4306/X2CrNi19-11/AISI304L不锈钢

Europa
EN

USA
UNS

USA
ASTM

China
GB

Russia
GOST

Giappone
JIS

India
IS

Corea
KS

X2CrNi19-11

S30403

304L

022Cr19Ni10

C%

max

Si%

max

Mn%

max

P%

max

S%

Cr%

Ni%

N%

max

EN 10088-1:2005

0.03

1.00

2.00

0.045

0.030

18.0-20.0

10.0-12.0

0.11

±0.005

±0.05

±0.04

±0.005

±0.005

±0.2

±0.15

±0.01

屈服强度
Yield Strength

N/mm2 min

抗拉强度
Tensile Sterength

N/mm2  

伸长率
Elong Ation  

A（%）min

面缩率
Reduction of Arca Z (%)

min

冲击功
Impace  

 AK(J）

硬度
Hardness

Max HB

180

460-680

45

215

+AT